Lidquid Glass...
Mar 23rd, 2015 at 11:06am
 
Like many of you, I've used CA or epoxy glues to seal cracks or other imperfections in blanks.  My wife recently used the product called 'Liquid Glass' and I was intrigued by the viscosity of the material.  When using epoxy I've experienced problem getting the material deep into cracks where I think the thinner viscosity of the Liquid Glass would allow the material to seep deeper into cracks.  Has anyone used this material and what are you experiences?  Any thoughts would be appreciated, thanks.
Back to top
  

“If history were taught in the form of stories, it would never be forgotten.”  Kipling
 
IP Logged
 
Register To Remove Ads
Dave Gill
Senior Member
****
Offline


Good People - Good Info!

Posts: 346

Hayward, California, USA
Hayward
California
USA

Gender: male

Jet 1220VS
Jet 1642EVS-2
Re: Lidquid Glass...
Reply #1 - Mar 23rd, 2015 at 1:10pm
 
I have not heard of "Liquid Glass" - know where to get it?

I usually use Epoxy with a little less Part B (Hardener) and force it down into the crack with a Popsicle Stick or tongue depressor (depending on the size of the crack). Less Part B gives a little more working time but then let it set overnight to make sure it has cured before working. If you are going to color the epoxy, mix it with the Part A before adding the Part B - again, gives you more working time.

Let us know about the "Liquid Glass" and where it can be found.

Thanks - Dave 
Back to top
  

I know I ask perfection of a quite imperfect world...and fool enough to think that's what I'll find!
 
IP Logged
 
John Grace
WR Addict
*****
Offline


Everyone needs a good
wingman...

Posts: 1,278

Bel Air, Maryland, USA
Bel Air
Maryland
USA

Re: Lidquid Glass...
Reply #2 - Mar 23rd, 2015 at 4:54pm
 
My wife found it both at our local Ace hdwe and I also know Home Depot carries it.  When I tried it, it had the viscosity of a 'heavy bodied' latex paint if that makes sense.  anyways, I tried it yesterday and am going to put the piece back on the lathe later this week to see what happens and will let you know.
Back to top
  

“If history were taught in the form of stories, it would never be forgotten.”  Kipling
 
IP Logged
 
Alan Hollar
Active Member
***
Offline


WR Rocks!

Posts: 105

Newland, North Carolina, USA
Newland
North Carolina
USA

Re: Lidquid Glass...
Reply #3 - Mar 24th, 2015 at 7:59am
 
This may be the product. A bar top epoxy finish, link here:
Multimedia File Viewing and Clickable Links are available for Registered Members only!!  You need to Login or Register
Back to top
  
 
IP Logged
 
Richard Pyle
Active Member
***
Offline


Carpe Lignum

Posts: 154

Oklahoma City, Oklahoma, USA
Oklahoma City
Oklahoma
USA

Gender: male
Re: Lidquid Glass...
Reply #4 - Apr 13th, 2015 at 1:20pm
 
I've considered doing that w/ our vacuum sealer we use in the kitchen. Wondering if it would work for stabilizing wood?
Back to top
  
 
IP Logged
 
David Hill
Senior Member
****
Offline


Using all Texas woods
but prefer Mesquite

Posts: 492

Cuero, Texas, USA
Cuero
Texas
USA

Gender: male

Nova 1624
Laguna 18/47
Robust American Beauty
Re: Lidquid Glass...
Reply #5 - Apr 16th, 2015 at 12:32pm
 
Basically it's what I use as my epoxy for cracks and voids-mixed with whatever mineral I want to use as color.  I like it because it starts out thin when first mixed so it can penetrate into cracks and if I want it thicker, I just let it set for a time then use it (depending on conditions--up to 45-60 min.).  It cures well and you're able to lathe or sand it without difficulty.  A plus is that if you need a little more fill, it sticks well to the prior application.  Only down side is that it takes about 24 hours to really set/cure well.
I've not had any issues with separation/moving and actually have had more bad outcomes with CA.
Back to top
« Last Edit: Apr 16th, 2015 at 12:33pm by David Hill »  

Everyday liberating nice things from ordinary chunks of wood---and I like gnarly wood, the outcome is nearly always better than the start.
 
IP Logged
 
Ken Vaughan
WR Addict
*****
Offline


Still learning

Posts: 3,685

Juneau, Alaska, USA
Juneau
Alaska
USA

Gender: male

Stubby 750
Jet 1014 vs
Bonnie Klein Lathe

Re: Lidquid Glass...
Reply #6 - Apr 17th, 2015 at 12:25pm
 
Richard Pyle wrote on Apr 13th, 2015 at 1:20pm:
I've considered doing that w/ our vacuum sealer we use in the kitchen. Wondering if it would work for stabilizing wood?


Not enough vacuum to work effectively with penetration (28 inches Hg desired).  I have been looking for the perfect opportunity to use a bit of cactus juice on a punky endgrain bowl blank - let it soak in -- and then heat to 180 degrees F to set it.   Then turn away the material to final finish.   I am expecting some discoloration is likely.

Could/should work for thin sections or shallow penetration in select situations though.
Back to top
« Last Edit: Apr 17th, 2015 at 12:26pm by Ken Vaughan »  
 
IP Logged
 
Willie Sims
Full Member
**
Offline


WR Rocks!

Posts: 51

Tyler, Texas, USA
Tyler
Texas
USA

Re: Lidquid Glass...
Reply #7 - Apr 24th, 2015 at 12:11am
 
I think I know of the material your talking about, be very careful turning, it's brittle.
My dad worked in a fiberglass pipe company for close to 20 years, and I've used different epoxies in model airplanes
The issue with using thinner epoxies is that they are easier to crack.
Back to top
  
 
IP Logged
 
Register To Remove Ads
Ray Stubbs
Active Member
***
Offline


WR Rocks!

Posts: 191

Columbia, Mo., USA
Columbia, Mo.
USA

Gender: male
Re: Lidquid Glass...
Reply #8 - Sep 16th, 2015 at 2:45pm
 
Does anyone know if this material/Liquid Glass can be used as a finish like wop?
Back to top
  
 
IP Logged
 
Glenn Jacobs
WR Addict
*****
Offline


JC L&S

Posts: 2,077

North DFW, Texas, Texas, USA
North DFW, Texas
Texas
USA

Gender: male

Powermatic 3520C
Re: Lidquid Glass...
Reply #9 - Sep 17th, 2015 at 12:24pm
 
Ray, you could use it as a finish. Apply very thin and be prepared to do a LOT of sanding to get rid of the runs as it is a SLOW cure-24 hours. I tried it and not again.  I will say it is not as sensitive to moisture as Alumilite.

Glenn J.
Back to top
  

Woodworking all my life. Turning since ~93
Glenn+J  
IP Logged
 
Ken Vaughan
WR Addict
*****
Offline


Still learning

Posts: 3,685

Juneau, Alaska, USA
Juneau
Alaska
USA

Gender: male

Stubby 750
Jet 1014 vs
Bonnie Klein Lathe

Re: Lidquid Glass...
Reply #10 - Sep 17th, 2015 at 1:42pm
 

I remembered reading about thin epoxy and one of the turning clubs on the east coast has an article posted that is applicable --

Multimedia File Viewing and Clickable Links are available for Registered Members only!!  You need to Login or Register

under tips and techniques  "Using Thin Epoxy"   

(This is Donna Banfield's home club -- she does some nice work)

Back to top
  
 
IP Logged
 
Ray Stubbs
Active Member
***
Offline


WR Rocks!

Posts: 191

Columbia, Mo., USA
Columbia, Mo.
USA

Gender: male
Re: Lidquid Glass...
Reply #11 - Sep 21st, 2015 at 6:31pm
 
Thanks Glen, I'll take your advice and not try it.
Back to top
  
 
IP Logged
 
David Schuelke
Full Member
**
Offline


WR Rocks!

Posts: 60

Beaumont, California, USA
Beaumont, California
USA

Gender: male

Laguna Revo 18 x 36 2hp
Re: Lidquid Glass...
Reply #12 - Oct 23rd, 2015 at 12:21pm
 
Are you using the epoxy to fill cracks on turned bowls prior to sanding or blanks that have not been put on the lathe yet?